Endang Kusdarjanti, Dwiyanti Feriana R, Eny Inayati

= http://dx.doi.org/10.20473/fmi.v52i3.5445
Abstract views = 2327 times | downloads = 1943 times


One of the stages of manufacture of denture metal framework that is sandblasting, ie cleaning the remnants of investment material after metal casting process and remnants of metal oxide on the surface. After fitting in the master model, then the metal framework dentures do sandblasting again until smooth before elektropolishing. The tools used are sandblaster, material Al2O3 (aluminum oxide) size of 250 lm. The time it takes about 1 minute, but the time of 1 minute when applied to student practicum D3 is still not clean and there are still remnants of planting material castings and metal oxide on the surface of the Co-Cr. Objective: To determine the effect of time on pembutan teeth iruan sandblasting the metal frame of the metal surface roughness Co-Cr. This study is experimental laboratories. A sample of tablet shape with a diameter of 7mm, 2mm thick metal. Number of samples 24 tablets were divided into 4 groups each group consisting of six tablet samples. Distribution of the sample group of the study are as follows; Group 1; Sandblasting metal surfaces with 250 µm Al2O3 time of 1 minute, Group 2; Sandblasting metal surfaces with Al2O3 250 ?m 2 minutes, Group 3; Sandblasting metal surfaces with Al2O3 250 µm 3 minutes, Group 4; the group did not do sandblasting. Data were analyzed with ANOVA statistical analysis of the lane with 0:05 significance level. If there is a significant difference between groups duiji with HSD test. There were significant differences in surface roughness Co-Cr metal between the control group without sprayed with the spray group at 1 minute, 2 minutes and 3 minutes. In conclusion, the surface of a metal frame that is not done sandblasting coarser than done sandblasting. The longer the time sandblasting increasingly produce a smooth surface of a metal frame. Sandblasting is perfectly need sufficient time is 2-3 minutes.


sand blasting; metal frameworks; surface roughness; CoCr alloy

Full Text:



Anonymous (none). Available from http://www.my-worldhut.com/. Accessed August 15, 2015

Anusavice K (2003). Phillips' Science of Dental Materials, 11th ed, Philadelphia, Saunders, p 358-370

Bousbaa C, Madjoubi MA, Hamidouche Z, Bouaouadja N (2003). Effect of sandblasting on soda lime glass properties. Engineering Journal of the University of Qatar 16, 125-138

Carpenter MA and Goodkind RJ (1979). Effect of varying surface texture on bond strength of one semiprecious and one nonprecious ceramo-alloy. The Journal of Prosthetic Dentistry 42, 86-95

Craig RG and Powers JM (2002). Restorative Dental Materials, 11th ed, St Louis, Mosby Elsevier, p 186-658

Franhouver JAV (none). Factors involved in microbial colonization of oral prostheses. Available from http://www.agd.org/supprot/articels/?ArtID=5010. Accessed August 1, 2008

Henderson DS (1995). Impression materials and procedures for removable partial dentures. In: McGivney GP and Castleberry DJ (eds). McCracken's Removable Partial Prosthodontics, St Louis, Mosby Elsevier, p 313-350

Hudis MM (1977). Dental Laboratory Prosthodontics, Philadelphia, WB Saunders

Knezovic-Zlataric D, Nemet M, Baucic I (2003). Laboratory fibrication procedures of a metal partial danture framework. Acta Stomat Croat 37, 95-98

Kueh ST and Reza F (2012). Evaluation of physical properties and casting accuracy of chrome-cobalt alloys with different casting systems and investments. Journal of Physical Science 23, 91-102

Kumar K, Ananda, Nadinger RK, Patil NP (2013). A comparative study of the effectiveness of metal surface treatment in controlling microleakage of two different metal and acrylic resin interface. Research and Reviews: Journal of Dental Sciences 1, 7-12

Loney RW (2011). Removable partial denture manual. Available from http://removpros.dentistry.dal.ca/ ewExternalFiles/RPD%20Manual%2011.pdf. Accessed November 12, 2015

Manappallil JJ (2003). Basic Dental Materials, 2nd ed, New Delhi, Jaypee Brothers Medical Publishers (P) Ltd, p 302-307

Noort R (2002). Introduction to Dental Materials, 2nd ed, St Louis, Mosby Elsevier, p 227-229

Pietnicki K, Wolowiec E, Klimek L (2014). The effect of abrasive blasting on the strength of a joint between dental porcelain and metal base. Acta Bioeng Biomech 16, 63-68

Pintadi H (2013). Kombinasi gigi tiruan kerangka logam dengan termoplastik. Jurnal PDGI 62, 45-47

Powers JM and Wataha JC (2008). Dental Materials Properties and Manipulation, 9th ed, St Louis, Mosby Elsevier, p 122-124

Prabowo T (2008). Desain cangkolan pada gigi tiruan kerangka logam dalam usaha mendapatkan retensi gigi tiruan. Bachelor Thesis. Universitas Sumatera Utara, Medan

Quirynen M and Bollen CM (1995). The influence of surface roughness and surface-free energy supra and subgingival plaque formation in man. J clin periodontol 22, 1-14

Renvert Dental Technology Team (2008). Model casting technique: analysis, planning, and manufacture. Available from http://www.renfert.com/ fileadmin/content/pdfs/Fibeln/Modellgussfibel/Modellgussfibel_gb.pdf. Accessed January 12, 2016

Saif corporation (2008). Abrasive blasting. Available from http://www.saif.com/_files/safetyhealthguides/ ss-434.pdf. Accessed January16, 2008

Singh K and Gupta N (2012). Injection molding technique for fibrication of flexible prosthesis for flexible thermoplastik danture base materials. World Journal of Dantistry 3, 303-307

Slatineanu L, Potarniche S, Coteata M, Grigoras I, Gherman L, Negoescu F (2011). Surface roughness at alumunium parts sand blasting. Proceedings in Manufacturing Systems 6, 69-74

Surmann H and Huser J (1998). Automatic electropolishing of cobalt chromium dental cast alloys with a fuzyy logic controller. Computers & Chemical Engineering 22, 1099-1111

Usdentaldepot (2016). Sandblasters. Available from http://www.usdentaldepot.com /usdd/1/usdd_ sand-blast.pdf. Accessed February 15, 2016

Wang CS, Chen KK, Tajima K, Nagamatsu Y, Kakigawa H, Kozono Y (2010). Effect of sandblasting media and steam cleaning on bond strength of titanium-porcelain. Dental Materials Journal 29, 381-391

Widiyarta IM, Parwata IM, Lokantara IP, Perangin-Angin D, Suryawiranata NA(2015). Kekasaran permukaan baja karbon sedang akibat proses sandblasting dengan variasi tekanan dan sudut penyemprotan. Available from http://eprints.unlam. ac.id/668/1/MAN%20-%2015.pdf. Accessed Februari 15, 2016


  • There are currently no refbacks.

Copyright (c) 2017 Endang Kusdarjanti, Dwiyanti Feriana R, Eny Inayati

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

Indexed By

View My Stats

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.