One of the stages of manufacture of denture metal framework that is sandblasting, ie cleaning the remnants of investment material after metal casting process and remnants of metal oxide on the surface. After fitting in the master model, then the metal framework dentures do sandblasting again until smooth before elektropolishing. The tools used are sandblaster, material Al2O3 (aluminum oxide) size of 250 lm. The time it takes about 1 minute, but the time of 1 minute when applied to student practicum D3 is still not clean and there are still remnants of planting material castings and metal oxide on the surface of the Co-Cr. Objective: To determine the effect of time on pembutan teeth iruan sandblasting the metal frame of the metal surface roughness Co-Cr. This study is experimental laboratories. A sample of tablet shape with a diameter of 7mm, 2mm thick metal. Number of samples 24 tablets were divided into 4 groups each group consisting of six tablet samples. Distribution of the sample group of the study are as follows; Group 1; Sandblasting metal surfaces with 250 µm Al2O3 time of 1 minute, Group 2; Sandblasting metal surfaces with Al2O3 250 ?m 2 minutes, Group 3; Sandblasting metal surfaces with Al2O3 250 µm 3 minutes, Group 4; the group did not do sandblasting. Data were analyzed with ANOVA statistical analysis of the lane with 0:05 significance level. If there is a significant difference between groups duiji with HSD test. There were significant differences in surface roughness Co-Cr metal between the control group without sprayed with the spray group at 1 minute, 2 minutes and 3 minutes. In conclusion, the surface of a metal frame that is not done sandblasting coarser than done sandblasting. The longer the time sandblasting increasingly produce a smooth surface of a metal frame. Sandblasting is perfectly need sufficient time is 2-3 minutes.

Keywords

sand blasting metal frameworks surface roughness CoCr alloy

Article Details

License

  • Folia Medica Indonesiana is a scientific peer-reviewed article which freely available to be accessed, downloaded, and used for research purposes. Folia Medica Indonesiana (p-ISSN: 2541-1012; e-ISSN: 2528-2018) is licensed under a Creative Commons Attribution 4.0 International License. Manuscripts submitted to Folia Medica Indonesiana are published under the terms of the Creative Commons License. The terms of the license are:

    Attribution ” You must give appropriate credit, provide a link to the license, and indicate if changes were made. You may do so in any reasonable manner, but not in any way that suggests the licensor endorses you or your use.

    NonCommercial ” You may not use the material for commercial purposes.

    ShareAlike ” If you remix, transform, or build upon the material, you must distribute your contributions under the same license as the original.

    No additional restrictions ” You may not apply legal terms or technological measures that legally restrict others from doing anything the license permits.

    You  are free to :

    Share ” copy and redistribute the material in any medium or format.

    Adapt ” remix, transform, and build upon the material.

How to Cite
Kusdarjanti, E., R, D. F., & Inayati, E. (2017). EFFECT OF SANDBLASTING TIME ON THE ROUGHNESS OF THE METAL COBALT-CHROMIUM (co-cr) DURING DENTURE METAL FRAMEWORK PRODUCTION. Folia Medica Indonesiana, 52(3), 160–168. https://doi.org/10.20473/fmi.v52i3.5445
Download Citation
Endnote/Zotero/Mendeley (RIS)
BibTeX

References

  1. Anonymous (none). Available from http://www.my-worldhut.com/. Accessed August 15, 2015
  2. Anusavice K (2003). Phillips' Science of Dental Materials, 11th ed, Philadelphia, Saunders, p 358-370
  3. Bousbaa C, Madjoubi MA, Hamidouche Z, Bouaouadja N (2003). Effect of sandblasting on soda lime glass properties. Engineering Journal of the University of Qatar 16, 125-138
  4. Carpenter MA and Goodkind RJ (1979). Effect of varying surface texture on bond strength of one semiprecious and one nonprecious ceramo-alloy. The Journal of Prosthetic Dentistry 42, 86-95
  5. Craig RG and Powers JM (2002). Restorative Dental Materials, 11th ed, St Louis, Mosby Elsevier, p 186-658
  6. Franhouver JAV (none). Factors involved in microbial colonization of oral prostheses. Available from http://www.agd.org/supprot/articels/?ArtID=5010. Accessed August 1, 2008
  7. Henderson DS (1995). Impression materials and procedures for removable partial dentures. In: McGivney GP and Castleberry DJ (eds). McCracken's Removable Partial Prosthodontics, St Louis, Mosby Elsevier, p 313-350
  8. Hudis MM (1977). Dental Laboratory Prosthodontics, Philadelphia, WB Saunders
  9. Knezovic-Zlataric D, Nemet M, Baucic I (2003). Laboratory fibrication procedures of a metal partial danture framework. Acta Stomat Croat 37, 95-98
  10. Kueh ST and Reza F (2012). Evaluation of physical properties and casting accuracy of chrome-cobalt alloys with different casting systems and investments. Journal of Physical Science 23, 91-102
  11. Kumar K, Ananda, Nadinger RK, Patil NP (2013). A comparative study of the effectiveness of metal surface treatment in controlling microleakage of two different metal and acrylic resin interface. Research and Reviews: Journal of Dental Sciences 1, 7-12
  12. Loney RW (2011). Removable partial denture manual. Available from http://removpros.dentistry.dal.ca/ ewExternalFiles/RPD%20Manual%2011.pdf. Accessed November 12, 2015
  13. Manappallil JJ (2003). Basic Dental Materials, 2nd ed, New Delhi, Jaypee Brothers Medical Publishers (P) Ltd, p 302-307
  14. Noort R (2002). Introduction to Dental Materials, 2nd ed, St Louis, Mosby Elsevier, p 227-229
  15. Pietnicki K, Wolowiec E, Klimek L (2014). The effect of abrasive blasting on the strength of a joint between dental porcelain and metal base. Acta Bioeng Biomech 16, 63-68
  16. Pintadi H (2013). Kombinasi gigi tiruan kerangka logam dengan termoplastik. Jurnal PDGI 62, 45-47
  17. Powers JM and Wataha JC (2008). Dental Materials Properties and Manipulation, 9th ed, St Louis, Mosby Elsevier, p 122-124
  18. Prabowo T (2008). Desain cangkolan pada gigi tiruan kerangka logam dalam usaha mendapatkan retensi gigi tiruan. Bachelor Thesis. Universitas Sumatera Utara, Medan
  19. Quirynen M and Bollen CM (1995). The influence of surface roughness and surface-free energy supra and subgingival plaque formation in man. J clin periodontol 22, 1-14
  20. Renvert Dental Technology Team (2008). Model casting technique: analysis, planning, and manufacture. Available from http://www.renfert.com/ fileadmin/content/pdfs/Fibeln/Modellgussfibel/Modellgussfibel_gb.pdf. Accessed January 12, 2016
  21. Saif corporation (2008). Abrasive blasting. Available from http://www.saif.com/_files/safetyhealthguides/ ss-434.pdf. Accessed January16, 2008
  22. Singh K and Gupta N (2012). Injection molding technique for fibrication of flexible prosthesis for flexible thermoplastik danture base materials. World Journal of Dantistry 3, 303-307
  23. Slatineanu L, Potarniche S, Coteata M, Grigoras I, Gherman L, Negoescu F (2011). Surface roughness at alumunium parts sand blasting. Proceedings in Manufacturing Systems 6, 69-74
  24. Surmann H and Huser J (1998). Automatic electropolishing of cobalt chromium dental cast alloys with a fuzyy logic controller. Computers & Chemical Engineering 22, 1099-1111
  25. Usdentaldepot (2016). Sandblasters. Available from http://www.usdentaldepot.com /usdd/1/usdd_ sand-blast.pdf. Accessed February 15, 2016
  26. Wang CS, Chen KK, Tajima K, Nagamatsu Y, Kakigawa H, Kozono Y (2010). Effect of sandblasting media and steam cleaning on bond strength of titanium-porcelain. Dental Materials Journal 29, 381-391
  27. Widiyarta IM, Parwata IM, Lokantara IP, Perangin-Angin D, Suryawiranata NA(2015). Kekasaran permukaan baja karbon sedang akibat proses sandblasting dengan variasi tekanan dan sudut penyemprotan. Available from http://eprints.unlam. ac.id/668/1/MAN%20-%2015.pdf. Accessed Februari 15, 2016