Evaluation of physical properties of glass ionomer cement modified by ethanolic extract of propolis
Downloads
Background: Glass ionomer cement (GIC) is a dental material often used in clinical practice. However, its use is limited due to its drawbacks. Natural resources such as propolis have been used to mainly enhance GIC’s antibacterial properties, but other properties attributed to this enhancement also require evaluation. Purpose: The study aims to evaluate the surface hardness, the surface roughness, and the water absorption of GIC containing ethanolic extract of propolis (EEP) from Trigona spp. Methods: Samples in this study were divided into four groups: GIC (control group); GIC + 25% EEP; GIC + 30% EEP; and GIC + 35% EEP. Surface roughness was measured using a surface roughness tester. Surface hardness was measured using a micro-Vickers hardness tester. Water absorption was measured by weighing the samples before and after immersion in distilled water. Surface characterization was carried out using a scanning electron microscope (SEM). Data was statistically analyzed using the Shapiro–Wilk normality test and one-way variance analysis along with the post-hoc Tukey’s test to determine significant differences between all four samples. Results: The statistical test showed significant differences in surface hardness and surface roughness between the control group and the GIC + EEP group. However, the test demonstrated no significant differences in water absorption between the control group and the GIC + EEP group. Conclusion: The addition of EEP to conventional GIC can affect its physical properties.
Downloads
Oliveira GL, Carvalho CN, Carvalho EM, Bauer J, Leal AMA. The influence of mixing methods on the compressive strength and fluoride release of conventional and resin-modified glass ionomer cements. Int J Dent. 2019; 2019: 6834931. doi: https://doi.org/10.1155/2019/6834931
Rizzante FAP, Cunali RS, Bombonatti JFS, Correr GM, Gonzaga CC, Furuse AY. Indications and restorative techniques for glass ionomer cement. Rev Sul-Brasileira Odontol. 2016; 12(1): 79–87. doi: https://doi.org/10.21726/rsbo.v12i1.733
Singh S, Mittal S, Tewari S. Effect of different liners on pulpal outcome after partial caries removal: A preliminary 12 months randomised controlled trial. Caries Res. 2019; 53(5): 547–54. doi: https://doi.org/10.1159/000499131
Saran R, Upadhya NP, Ginjupalli K, Amalan A, Rao B, Kumar S. Effect on physical and mechanical properties of conventional glass ionomer luting cements by incorporation of all-ceramic additives: An in vitro study. Int J Dent. 2020; 2020: 8896225. doi: https://doi.org/10.1155/2020/8896225
Ching HS, Luddin N, Kannan TP, Ab Rahman I, Abdul Ghani NRN. Modification of glass ionomer cements on their physical"mechanical and antimicrobial properties. J Esthet Restor Dent. 2018; 30(6): 557–71. doi: https://doi.org/10.1111/jerd.12413
Ranjbar Omrani L, Moradi Z, Abbasi M, Kharazifard MJ, Tabatabaei SN. Evaluation of compressive strength of several pulp capping materials. J Dent (Shiraz, Iran). 2021; 22(1): 41–7. doi: https://doi.org/10.30476/dentjods.2020.83964.1063
Nur Karakaş S, Turgut H, Küde C. Comparison of surface roughness and microhardness of reinforced glass ionomer cements and microhybrid composite. J Dent Indones. 2021; 28(3): 131–8. doi: https://doi.org/10.14693/jdi.v28i3.1232
Spinola M, Dal Piva AMO, Barbosa PU, Torres CRG, Bresciani E. Mechanical assessment of glass ionomer cements incorporated with multi-walled carbon nanotubes for dental applications. Oral. 2021; 1(3): 190–8. doi: https://doi.org/10.3390/oral1030019
Altunsoy M, Tanrıver M, Türkan U, Uslu ME, Silici S. In vitro evaluation of microleakage and microhardness of ethanolic extracts of propolis in different proportions added to glass ionomer cement. J Clin Pediatr Dent. 2016; 40(2): 136–40. doi: https://doi.org/10.17796/1053-4628-40.2.136
Hasan AEZ, Mangunwidjaja D, Sunarti TC, Suparno O, Setiyono A. Optimasi ekstraksi propolis menggunakan cara maserasi dengan pelarut etanol 70% dan pemanasan gelombang mikro serta karakterisasinya sebagai bahan antikanker payudara. J Teknol Ind Pertan. 2013; 23(1): 13–21. web: https://journal.ipb.ac.id/index.php/jurnaltin/article/view/7230
Riendriasari SD, Krisnawati K. Produksi propolis mentah lebah madu Trigona spp. di pulau Lombok. ULIN J Hutan Trop. 2017; 1(1): 71–5. doi: https://doi.org/10.32522/ujht.v1i1.797
El Ghazouly Y, Sharaf A, Hanafy S, El Habashy LM. Assessment of microleakage and microhardness of glass ionomer cement containing propolis: In vitro study. Alexandria Dent J. 2021; 46(2): 172–7. doi: https://doi.org/10.21608/adjalexu.2020.28760.1061
Mushtaq U, Mushtaq F, Thakur D, Rathee K, Poonia N, Khullar S. Comparative evaluation of postoperative sensitivity following restoration of class I lesions with different restorative materials: An in vivo study. J Contemp Dent Pract. 2021; 22(6): 650–4. pubmed: http://www.ncbi.nlm.nih.gov/pubmed/34393122
Tjandrawinata R, Irie M, Suzuki K. Flexural properties of eight flowable light-cured restorative materials, in immediate vs 24-hour water storage. Oper Dent. 2005; 30(2): 239–49. pubmed: http://www.ncbi.nlm.nih.gov/pubmed/15853111
Kovianti C, Tjandrawinata R, Eddy E. Mechanical properties of giomer after immersion in carbonated drinks. J Indones Dent Assoc. 2023; 5(2): 79–84. doi: https://doi.org/10.32793/jida.v5i2.786
Davidovic L, Stojanovic N, Krunic J, Zivkovic S. Scanning electron microscopy analysis of adhesive bond of glass-ionomer cement restorations. Stomatol Glas Srb. 2013; 60(2): 85–92. doi: https://doi.org/10.2298/SGS1302085D
Subramaniam P, Girish Babu K, Neeraja G, Pillai S. Does addition of propolis to glass ionomer cement alter its physicomechanical properties? An in vitro study. J Clin Pediatr Dent. 2016; 40(5): 400–3. doi: https://doi.org/10.17796/1053-4628-40.5.400
Megawati G, Wijayakesuma A. Literature review: Potensi propolis sebagai imunomodulator. J Kesehat. 2022; 13(3): 636. doi: https://doi.org/10.26630/jk.v13i3.2742
Topcuoglu N, Ozan F, Ozyurt M, Kulekci G. In vitro antibacterial effects of glass-ionomer cement containing ethanolic extract of propolis on Streptococcus mutans. Eur J Dent. 2012; 6(4): 428–33. pubmed: http://www.ncbi.nlm.nih.gov/pubmed/23077424
Anjum SI, Ullah A, Khan KA, Attaullah M, Khan H, Ali H, Bashir MA, Tahir M, Ansari MJ, Ghramh HA, Adgaba N, Dash CK. Composition and functional properties of propolis (bee glue): A review. Saudi J Biol Sci. 2019; 26(7): 1695–703. doi: https://doi.org/10.1016/j.sjbs.2018.08.013
Azalia A, Pratiwi D, Hasan AZ, Tjandrawinata R, Eddy E. In vitro evaluation of the compressive strength of glass ionomer cement modified with propolis in different proportions. Sci Dent J. 2023; 7(1): 6–10. doi: https://doi.org/10.4103/SDJ.SDJ_1_23
MiliÄević A, GorÅ¡eta K, van Duinen R, Glavina D. Surface roughness of glass ionomer cements after application of different polishing techniques. Acta Stomatol Croat. 2018; 52(4): 314–21. doi: https://doi.org/10.15644/asc52/4/5
Wulandari E, Wardani FRA, Fatimattuzahro N, Dewanti IDAR. Addition of gourami (Osphronemus goramy) fish scale powder on porosity of glass ionomer cement. Dent J. 2022; 55(1): 33–7. doi: https://doi.org/10.20473/j.djmkg.v55.i1.p33-37
Pratiwi D, Salim RF, Tjandrawinata R, Komariah K. Evaluasi morfologi permukaan semen ionomer kaca dengan modifikasi penambahan nanokitosan kumbang tanduk Surface morphology evaluation of glass ionomer cement modified with nano chitosan of rhinoceros beetle. J Kedokt Gigi Univ Padjadjaran. 2021; 33(3): 240. doi: https://doi.org/10.24198/jkg.v33i3.32231
Eriwati YK, Dhiaulfikri M, Herda E. Effect of salivary pH on water absorption and solubility of enhanced resin- modified glass ionomer. J Dent Indones. 2020; 27(3): 164–9. doi: https://doi.org/10.14693/jdi.v27i3.1199
Copyright (c) 2024 Dental Journal
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
- Every manuscript submitted to must observe the policy and terms set by the Dental Journal (Majalah Kedokteran Gigi).
- Publication rights to manuscript content published by the Dental Journal (Majalah Kedokteran Gigi) is owned by the journal with the consent and approval of the author(s) concerned.
- Full texts of electronically published manuscripts can be accessed free of charge and used according to the license shown below.
- The Dental Journal (Majalah Kedokteran Gigi) is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License